NANOTEC MACHINE-APPLIED UNIVERSAL PLASTER

Product description

Gypsum based multipurpose plaster for machine application, enriched with mixtures expanding opportunities of the product application, enhancing heat and sound insulation, substituting cement and sand based plaster, as well as plaster primer and white plasters, creating even, brilliant and defect-free surface.

The product conforms to the requirements of the AZS 052 (TS 6433) standard.

Fields of Application

This product can be applied in the following areas:

high quality mechanical plastering for walls and ceilings of industrial and civil buildings built from bricks, construction stone, briquettes (coal, peat, ore pressed in the shape of bricks), concrete, and gas concrete, applied using plastering machines;

forms even, defect-free and brilliant surfaces.

Advantages

In case of application in large-scale construction projects makes the repair operations faster and more cost effective ;

Saves working time;

Easy application;

Does not form cracks;

Provides air permeability to rooms;

Has higher decoration advantages;

Excellent convenience of use;

Environmentally friendly, does not produce dusting;

Does not require mixing with PVA adhesives;

Decreases the load bearing capacity of the structures compared to the wall surfaces treated with plaster primer;

Makes the operator's work much easier;

Application procedures

Preparation of the surface. Please pay attention to the treated surface: it should be firm and free of residues deteriorating adhesive force (dust, oil, etc). Machine equipment used for preparation of NANOTEC machine plaster should be clean and should be in good operating conditions. Before the NANOTEC machine plaster application the surface should be thoroughly dampened. In order to make the plastered surface even  aluminum shapes should be placed under the guide screeds. In order to prevent breaking of wall corners and to make them even and regular shape it is necessary to place special angle sections in the corners. Points of connection of different materials and areas of possible movement should be provided with a special plastic lath for plaster. In case the surface is too smooth, there is no need to use handicraft methods to make it rough. To provide surface strength and prevent spalling, such surfaces should be treated with EPOKONTAKT plaster bonding coat which provides two-way bonding effect between the base surface and the applied plaster. This should be done 24 hours prior to application of the plaster. Metal surfaces should be protected from corrosion by means of treatment with anti-corrosion solution prior to application of  NANOTEC  machine plaster.

Preparation of the mixture. Place the required amount of NANOTEC product into the plaster machine bin, then supply continuous flow of water into the machine. Input the data on water and NANOTEC powder proportion into the machine program, then start up the machine and mix the components automatically till the mixture is entirely homogeneous. Do not add to NANOTEC  product any additives or substances other than water.

Application. The prepared machine plaster is applied by spray gun onto the surface prepared for application (between the installed guide screed strips). The spray gun is driven by air compressor installed in the plaster machine and should form the layer at least 10 mm thick. The NANOTEC consumption of the plaster machine may differ and depends on the surface type.

The plaster sprayed onto the surface should be smoothed using special plaster rasp (aluminum shape), and the excessive amounts of the mixture should be removed. If the plaster pressed with a finger does not adhere to the finger, the surface may be smoothed with the rasp trowel.

In approximately 1 hour the surface should be dampened with a sponge and then, in 10-15 minutes the thin top layer of the plaster should be pressed with a finger and if the finger remains clean, then the surface may be smoothed using metal rasp trowel. This will form a defect-free brilliant surface.

In case the required plaster layer thickness is below 3 mm, then one layer of NANOTEC machine plaster should be applied. In case the required plaster layer thickness is above 3 mm, it is necessary to apply the second layer. This second layer should be applied in approximately 2 hours after application of the first layer (if the plaster pressed with a finger does not adhere to the finger). In case the machine plaster layer applied exceeds 3 mm thickness, then irregularities may occur on the surface due to the weight of the mixture applied, and this may require application of the second layer.

Recommendations. At the time of plaster application the ambient and surface temperatures should be +50C minimum. If at the time of application the ambient temperature exceeds the limits of +50C - +300C range, then the required temperature level should be provided. The product should not be used in warm (above +300C), rainy and windy weather conditions. The can and the equipment used for preparation of the mixture should always be clean. After use all hand tools and devices should be immediately cleaned with water. Dirty cans and tools reduce the useful life of the mixture.

When using the metal trowel pay special attention to avoiding traces left on the surface. Provide continuous supply of water to the machine (equipment).

Consumption
The NANOTEC machine plaster consumption at minimum 10 mm thick layer is 9 kg/m2. 1 sack (30 kg) of NANOTEC machine plaster is enough to cover even surface of approximately 3 m2 area.

Shelf Life and Storage Method

The product can be stored during 6 months in packaged sacks in closed areas, in dry conditions, on wooden racks, maximum 10 sacks per rack placed one over another, provided that they do not contact with the floor.


Warnings

pay special attention to clean conditions of the cans and water used for preparation;

do not add to the primer any substances other than water;

parameters indicated above have been received on the basis of laboratory tests conducted in the ambient conditions of +230C±20C temperature and 50% + 5% humidity. Depending on the actual ambient conditions these parameters are subject to change.

Warranty and technical support

information indicated in technical specifications is based on scientific and experimental data;

EPO company is responsible for the product quality only;

with the exception of cases of works executed under the supervision of the company specialists, EPO company shall not be liable for any problems occuring due to improper use of the product by other persons;

the company reserves the right to make changes in its product in consequence of scientific-and-technical development;

for technical support and/or more information please do not hesitate to contact the EPO compani